Feature:
substantially higher thermal conductivity, very low friction coefficient, higher fracture strength and fracture toughness
Application:
cutting (machining) non-ferrous materials, ceramics, abrasive composites, high silicon-content aluminium alloy, graphite, and other difficult machining materials.
*Supplied different dimension as required
Vickers Hardness | 8000-10000kg/mm² |
Density | 3.51g/cm³ |
Young's Modulus | 1000-1100GPa |
Thermal Conductivity | ＞1000W/m·K |
Specific Heat | 0.52J/gK |
Break Strength | ＞500MPa (Film thickness0.5mm, Force on growth surface) |
Thermal Stability | Maintained at 800℃ for 10 minutes, the mechanical strength remains unchanged |
Wear Ratio | ＞300000 |
Chemical Stability | Insoluble in all of acid and alkali |
Color | Semi Transparency |
Feature:
substantially higher thermal conductivity, very low friction coefficient, higher fracture strength and fracture toughness
Application:
cutting (machining) non-ferrous materials, ceramics, abrasive composites, high silicon-content aluminium alloy, graphite, and other difficult machining materials.
*Supplied different dimension as required
Vickers Hardness | 8000-10000kg/mm² |
Density | 3.51g/cm³ |
Young's Modulus | 1000-1100GPa |
Thermal Conductivity | ＞1000W/m·K |
Specific Heat | 0.52J/gK |
Break Strength | ＞500MPa (Film thickness0.5mm, Force on growth surface) |
Thermal Stability | Maintained at 800℃ for 10 minutes, the mechanical strength remains unchanged |
Wear Ratio | ＞300000 |
Chemical Stability | Insoluble in all of acid and alkali |
Color | Semi Transparency |