As a alternative to natural and Monocrystal diamonds, it is suitable for all dresser types - single point, multipoint, blade, rotary, roller etc
Product Grade:
YLH grade: suitable for common diamond dresser tools
YLG grade: high wear resistance, to be substitute of nature and HTHP synthetic single crystal diamond.
Main Data | YLH Grade | YLG Grade |
Vickers hardness (kg/mm²) | 8000 | 10000 |
Density（g/cm³） | 3.51 | 3.51 |
Young's modulus(Gpa) | 1000 | 1100 |
Thermal conductivity (W/m·K) | ＞1000 | ＞1500 |
Chemical stability | insoluble in all acids and alkali | |
Break strength(Mpa) | 350 | 550 |
Thermal stability | 800 ℃ | 800 ℃ |
Wear ratio | 200000 | 400000 |
As a alternative to natural and Monocrystal diamonds, it is suitable for all dresser types - single point, multipoint, blade, rotary, roller etc
Product Grade:
YLH grade: suitable for common diamond dresser tools
YLG grade: high wear resistance, to be substitute of nature and HTHP synthetic single crystal diamond.
Main Data | YLH Grade | YLG Grade |
Vickers hardness (kg/mm²) | 8000 | 10000 |
Density（g/cm³） | 3.51 | 3.51 |
Young's modulus(Gpa) | 1000 | 1100 |
Thermal conductivity (W/m·K) | ＞1000 | ＞1500 |
Chemical stability | insoluble in all acids and alkali | |
Break strength(Mpa) | 350 | 550 |
Thermal stability | 800 ℃ | 800 ℃ |
Wear ratio | 200000 | 400000 |